GB/T 30984.3-2016Solar glass—Part 3: Reflective glass mirror (English PDF)
太阳能用玻璃 第3部分：玻璃反射镜
This is a limited preview
Buy now to download the full PDF (27 pages)
Need quotation for your management?
Get a formal quotation for GB/T 30984.3-2016 in 30 minutes.
Issued by
SAMR; SAC
Level / Type
National · Recommended
Issue date
December 13, 2016
Implementation date
November 1, 2017
Scope
GB/T 30984.3-2016 is the English-translated version of 太阳能用玻璃 第3部分：玻璃反射镜.
GB/T 30984.3-2016 is the Chinese standard "Solar glass - Part 3: Reflective glass mirror". Its scope clause reads: This part of GB/T 30984 specifies the terms and definitions, classification and common specifications, materials, requirements, test methods, inspection rules, packaging, marking, storage and transportation of reflective glass mirrors.
This part applies to solar thermal reflective glass mirrors, condenser photovoltaic mirrors and other types of mirrors can be implemented with reference to this part.
Its clauses include terms and definitions; classifications and common specifications; materials; requirements; inspection rules. It was issued by the General Administration of Quality Supervision, Inspection and Quarantine on DECEMBER 13, 2016 and took effect on DECEMBER 01, 2017.
Found what you need?
Document preview — GB/T 30984.3-2016
National Standard of the People's Republic of China
- ICS
- 81.040.30
- Classification
- Q 34
Issued by: State Administration for Market Regulation; Standardization Administration of the PRC
Contents
- Foreword3
- 1 Scope4
- 2 Normative references4
- 3 Terms and definitions5
- 4 Classifications and common specifications6
- 5 Materials6
- 6 Requirements7
- 7 Test methods13
- 8 Inspection rules21
- 9 Packaging, marking, storage and transportation25
- Appendix A (Normative) Surface shape accuracy27
Foreword
GB/T 30984 "Solar glass" is currently divided into 3 parts.
- Part 1. Ultra-clear patterned glass;
- Part 2. Transparent conductive oxide coated glass;
- Part 3. Reflective glass mirror.
This section is Part 3 of GB/T 30984.
This part was drafted in accordance with the rules given in GB/T 1.1-2009.
1 Scope
This part of GB/T 30984 specifies the terms and definitions, classification and common specifications, materials, requirements, test methods, inspection rules, packaging, marking, storage and transportation of reflective glass mirrors.
This part applies to solar thermal reflective glass mirrors, condenser photovoltaic mirrors and other types of mirrors can be implemented with reference to this part.
2 Normative references
The following documents are essential to the application of this document. For the dated documents, only the versions with the dates indicated are applicable to this document; for the undated documents, only the latest version (including all the amendments) are applicable to this standard.
GB/T 531.1 Rubber vulcanized or thermoplastic - Determination of indentation hardness - Part 1: Durometer method (Shore hardness)
GB/T 2423.3 Environmental testing for electric and electronic products - Part 2: Testing method test Cab. Damp heat Steady state (GB/T 2423.3-2006, IEC 60068-2-78:2001, IDT)
GB/T 2828.1-2012 Sampling procedures for inspection by attributes - Part 1:
Sampling schemes indexed by acceptance quality limit (AQL) for lot-by-lot inspection (GB/T 2828.1-2012, ISO 2859.1:1999, IDT)
GB/T 5137.3 Road vehicles - Safety glazing materials - Test methods for resistance to radiation high temperature humidity fire and simulated weathering
GB/T 8170 Rules of rounding off for numerical values & expression and judgement of limiting values
GB/T 9056 Steel ruler
GB/T 9286 Paints and varnishes - Cross cut test for films (GB/T 9286-1998, eqv ISO 2409:1992)
GB/T 10125 Corrosion tests in artificial atmospheres - Salt spray tests (GB/T appearance quality shall comply with the requirements in Table 1.
6 Requirements
6.9 Neutral salt spray (NSS) test performance
It is tested in accordance with 7.10, after the test, the surface of the protective coating of the monolithic reflective glass mirror test shall have no peeling, cracks, and stripping, and the reflective layer shall not subject to discoloration or turbidity. The appearance quality meets the requirements of Table 1, the edge corrosion shall not be greater than 1.0 mm; the composite reflective glass mirror shall have no open glue after the test, the part 1.0 m beyond the edge is free from air bubble or coating loss, there is no change at the front surface of the specimen during visual observation, the appearance quality shall comply with the requirements in Table 1.
6.10 Copper accelerated acrylate spray (CASS) test performance
It is tested accordance with 7.11, after the test, the protective coating surface of the monolithic reflective mirror shall be free from peeling, cracking, or stripping, the reflective layer shall not discolor or turbid, the appearance quality complies with the requirements of Table 1, the edge corrosion shall not be more than 1.5 mm; the composite reflective glass mirror shall have no open glue after the test, the part 1.5 m beyond the edge is free from air bubble or coating loss, there is no change at the front surface of the specimen during visual observation, the appearance quality shall comply with the requirements in Table 1.
6.11 Heat cycle resistance
It is tested in accordance with 7.12, after the test, the attenuation of the solar hemispherical reflectance shall not exceed 1.5%. After the monolithic reflective glass mirror test, the surface of the protective coating shall be free from peeling, cracks, and stripping. The reflective layer shall not be discolored or turbid. The appearance quality meets the requirements of Table 1, the edge corrosion shall not exceed 1.5 mm; the composite reflective glass mirror shall have no open glue after the test, the part 1.5 m beyond the edge is free from air bubble or coating loss, there is no change at the front surface of the specimen during visual observation, the appearance quality shall comply with the requirements in Table 1.
6.12 Frost resistance
It is tested in accordance with 7.13 based on the conditions of use as negotiated between the supplier and the purchaser, after the test, the attenuation of the solar hemispherical reflectance shall not exceed 1.5%. After the monolithic reflective glass mirror test, the surface of the protective coating shall be free from peeling, cracks, and stripping. The reflective layer shall not be discolored or turbid. The appearance quality meets the requirements of Table 1, the edge corrosion shall not exceed 1.5 mm; the composite reflective glass mirror shall have no open glue after the test, the part 1.5 m beyond the edge is free from air bubble or coating loss, there is no change at the front surface of the specimen during visual observation, the appearance quality shall comply with the requirements in Table 1.
6.13 Damp heat resistance
It is tested in accordance with 7.14 based on the conditions of use as negotiated between the supplier and the purchaser, after the test, the attenuation of the solar hemispherical reflectance shall not exceed 1.5%. After the monolithic reflective glass mirror test, the surface of the protective coating shall be free from peeling, cracks, and stripping. The reflective layer shall not be discolored or turbid. The appearance quality meets the requirements of Table 1, the edge corrosion shall not exceed 1.5 mm; the composite reflective glass mirror shall have no open glue after the test, the part 1.5 m beyond the edge is free from air bubble or coating loss, there is no change at the front surface of the specimen during visual observation, the appearance quality shall comply with the requirements in Table 1.
6.14 UV radiation resistance
It is tested in accordance with 7.15, after the test, the attenuation of the solar hemispherical reflectance shall not exceed 1%. After the monolithic reflective glass mirror test, the surface of the protective coating shall be free from peeling, cracks, and stripping. The reflective layer shall not be discolored or turbid. The appearance quality meets the requirements of Table 1, the edge corrosion shall not exceed 1.5 mm; the composite reflective glass mirror shall have no open glue after the test, the part 1.5 m beyond the edge is free from air bubble or coating loss, there is no change at the front surface of the specimen during visual observation, the appearance quality shall comply with the requirements in Table 1.
6.15 Wear resistance
6.15.1 Mirror surface wear resistance
It is tested in accordance with 7.16.1, the solar hemispherical reflectance change caused by abrasion after the test shall not exceed 1.0%.
6.15.2 Protective layer wear resistance
For monolithic reflective glass mirror, one piece is taken to perform test in accordance with 7.16.2, after the test, the primer shall not be exposed, the protective layer appearance shall be free from obvious change during visual observation.
6.16 Protective layer adhesion
A sample that has a size of 300 mm x 300 mm prepared in the same material as the product and under the same process conditions is used as a specimen, the number is 3 pieces. It is tested in accordance with the provisions of GB/T 5137.3.
7 Test methods
7.9 Condensate test performance
7.9.1 Specimen
A sample that has a size of at least 100 mm×70 mm prepared in the same material as the product and under the same process conditions is used as a specimen, the number is 3 pieces.
7.9.2 Test procedure
It is tested in accordance with the provisions of GB/T 13893, the test time is 480 h. […]
7.10 Neutral salt spray (NSS) test performance
7.10.1 Specimen
......
This preview omits tables, figures, formulas and parts of the technical clauses. The complete document — 27 pages — is available in the English PDF.
Referenced standards
Normative references
- GB/T 531.1Rubber, vulcanized or thermoplastic -- Determination of indentation hardness -- Part 1: Durometer method (Shore hardness)
- GB/T 2423.3Environmental testing - Part 2: Testing method - Test Cab: Damp heat, steady state
- GB/T 2828.1-2012Sampling procedures for inspection by attributes - Part 1: Sampling schemes indexed by acceptance quality limit (AQL) for lot-by-lot inspection
- GB/T 5137.3Test methods of safety glazing materials used on road vehicles - Part 3: Radiation, high temperature, humidity, fire and simulated weathering resistance tests
- GB/T 8170Rules of rounding off for numerical values & expression and judgement of limiting values
- GB/T 9056Metal ruler
Similar standards
How to Download GB/T 30984.3-2016
- 1
Add to cart
Click "Download PDF" on this page and choose "Buy this standard". You can add more standards before checkout.
- 2
Checkout
Enter your email and billing details. Payment is processed securely by Stripe (cards or bank transfer). Prefer bank details? Request a quotation (min. order $300).
- 3
Instant delivery (0–9 sec)
Delivery is automatic: within seconds of payment you'll receive an email with a secure download link. The link stays valid for 72 hours.
- 4
Invoice included
A tax invoice is attached to the confirmation email. Need a custom invoice? Contact us.
Related Standards
GB/T 10125-2021 — Corrosion tests in artificial atmospheres - Salt spray tests
GB/T 2423.3-2016 — Environmental testing - Part 2: Testing method - Test Cab: Damp heat, steady state
GB/T 2423.30-2013 — Environmental testing - Part 2: Test methods - Test XA and guidance: Immersion in cleaning solvents