GB/T 31923.1-2015Iron ores for blast furnace feedstocks -- Determination of low-temperature reduction-disintegration indices by static method -- Part 1: Reduction with CO, CO2, H2 and N2 (English PDF)

Foreword

GB/T 31923 "for blast furnace iron ore RDI static test" is divided into two parts.

--- Part 1. reaction with CO, CO2, H2 and N2 in;

--- Part 2. the reaction with CO and N2.

This section GB/T Part of 131,923.

This section drafted in accordance with GB/T 1.1-2009 given rules.

This section uses redrafted Law Amendment uses ISO 4696-1:2007 "for blast furnace iron ore RDI static test Part 1 of the reaction with CO, CO2, H2 and N2 is "(in English).

This part of ISO 4696-1:2007 technical differences and the reasons are as follows.

--- On normative references, this part has been adjusted technical differences, in order to adapt our technical conditions, the adjusted situation Focus is reflected in the status of Chapter 2, "Normative references", the specific adjustments are as follows.

(A) with a modified adoption of international standards of GB/T 6003.1 replaces ISO 3310-1 (see 6.8);

(B) with a modified adoption of international standards of GB/T 6003.2 replaces ISO 3310-2 (see 6.8);

(C) equivalents adoption of international standards GB/T 10322.1 instead of ISO 3082 (see 5.1);

(D) using identical with international standards GB/T 10322.7 instead of ISO 4701 (see 8.4);

(E) equivalents adoption of international standards GB/T 20565 replaces ISO 11323 (see Chapter 3).

This part is proposed by the China Iron and Steel Association.

This part of the National Iron ore and direct reduced iron Standardization Technical Committee (SAC/TC317) centralized.

This section is drafted. Shougang Corporation, Anshan Kexiang Instrument Co., Ltd., Shangyu Hongxing Machinery Instrument Manufacturing Co.

1 Scope

GB/T 31923 provisions of this part of the blast furnace is measured test CO, CO2, H2 and N2 after reduction of iron ore with a degree of chalking Test methods, test conditions similar to the main blast furnace low temperature reduction zone.

This section applies to lump ore, sinter and pellets of low RDI static test.

2 Normative references

The following documents for the application of this document is essential. For dated references, only the dated version suitable for use herein Member. For undated references, the latest edition (including any amendments) applies to this document.

GB/T 6003.1 Test sieves - Technical requirements and testing - Part 1. Test sieves of metal wire braid (GB/T 6003.1-2012, ISO 3310-1:2000, MOD) GB/T 6003.2 Test sieves - Technical requirements and testing - Part 2. Test sieves of perforated metal plate (GB/T 6003.2-2012, ISO 3310-2:1999, MOD) GB/T 10322.1 iron ore sampling and sample preparation method (GB/T 10322.1-2014, ISO 3082:2009, IDT) GB/T 10322.7 ore particle size distribution by sieving (GB/T 10322.7-2004, ISO 4701:1999, IDT) GB/T 20565 term iron ore and direct reduced iron (GB/T 20565-2006, ISO 11323:2002, IDT)

3 Terms and Definitions

Terms and definitions GB/T 20565 apply to this document defined.

Principle 4

Certain size range of the test sample, reducing gas in a fixed bed 500 °C with CO, CO2, H2 and N2 consisting of isothermal also Original 60min. The test sample after reduction with the drum rotation 300 rpm. Then respectively 6.30mm, 3.15mm and into the square hole sieve 500µm Line screening. Reduction degradation index (RDI) is calculated using the value of 6.30mm, 3.15mm, -3.15mm and -500µm test sample mass After reducing the amount of, respectively, in the percentage ratio of the total mass of the test sample before the drum.

5 Sampling, sample preparation and test sample preparation